English  |  正體中文  |  简体中文  |  Items with full text/Total items : 18054/20253 (89%)
Visitors : 24216537      Online Users : 60
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version
    Please use this identifier to cite or link to this item: https://ir.cnu.edu.tw/handle/310902800/34361


    標題: Effect of Anodization Treatment on the Thickness, Hardness, and Microstructural Characterization of Anodic Aluminum Oxide Film on AA 6061 and Critical Patent Analysis
    作者: Lee, Chun-Chieh
    Chen, Chih-Wei
    Lin, Jin-Shyong
    Wang, Shing Hoa
    Lee, Chiang-Sheng
    Chen, Chien-Chon
    Lin, Ya-Hui
    Chen, Chih-Yuan
    貢獻者: Natl United Univ, Coll Engn & Sci
    Chi Mei Med Ctr, Div Neurosurg, Dept Surg
    Chia Nan Univ Pharm & Sci, Dept Occupat Safety & Hlth, Inst Ind Safety & Disaster Prevent
    Natl Chin Yi Univ Technol, Dept Mech Engn
    Natl Taiwan Ocean Univ, Dept Mech & Mechatron Engn
    Natl United Univ, Dept Energy Engn
    Natl Taipei Univ Technol, Grad Inst Intellectual Property
    關鍵字: AA 6061
    anodization
    efficiency
    hardness
    oxide
    pre-treatment
    日期: 2021
    上傳時間: 2023-11-11 11:46:52 (UTC+8)
    出版者: SPRINGER
    摘要: The influences of different pre-treatment approaches, comprising sandblasting, grinding, chemical polishing, and plowing, and various anodizing parameters, including electrolyte composition, temperature, current density, time, and final voltage, on the quality of anodized aluminum oxide (AAO) film on AA 6061 were studied in the present research. It was found that, during both mild and hard anodization treatment, the thickness and microhardness of AAO film increased as the anodization current density increased. Under mild anodization treatment, when the current density increased from 0.5 to 2.0 A/dm(2), the anodization efficiency decreased from 90 to 52% and 71 to 44% during the mild anodization treatment performed at 22 degrees C and 0 degrees C, respectively. However, on the other hand, the anodization efficiency increased from 55 to 56% and 57 to 64% when the current density increased from 7.0 to 8.0 A/dm(2) during the hard anodization treatment carried out at 22 degrees C and 0 degrees C, respectively. Therefore, different AAO film formation mechanisms prevail during the mild and hard anodization treatment. Moreover, the microhardness of AAO film formed at 22 degrees C or 0 degrees C dropped heavily when the current density was higher than 9.0 A/dm(2) due to the burning reaction. In addition, the AAO film can achieve higher hardness and resistance to corrosion through the sealing process, which can effectively decrease the size of the tubes due to the volume expansion effect (23%) after the sealing treatment.
    關聯: J MATER ENG PERFORM, v.31, n.1, pp.667-681
    Appears in Collections:[職業安全衛生系(含防災所)] 期刊論文

    Files in This Item:

    File Description SizeFormat
    index.html0KbHTML120View/Open


    All items in CNU IR are protected by copyright, with all rights reserved.


    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback