Effect of a low-molecular-weight compatibilizer on the immiscible blends of cellulose acetate propionate and poly(butylene terephthalate)

doi:10.1007/s10965-018-1487-5

Chia Nan University of Pharmacy & Science Institutional Repository > 藥理學院 > 化妝品應用與管理系(所) > 期刊論文 > Item 310902800/32282

請使用永久網址來引用或連結此文件: https://ir.cnu.edu.tw/handle/310902800/32282

標題:	Effect of a low-molecular-weight compatibilizer on the immiscible blends of cellulose acetate propionate and poly(butylene terephthalate)
作者:	Liang, Nai-Yun Don, Trong-Ming Huang, Chih-Yuan Lee, Chia-Fen Chiu, Wen-Yen
貢獻者:	Natl Taiwan Univ, Inst Polymer Sci & Engn Tamkang Univ, Dept Chem & Mat Engn Chia Nan Univ Pharm & Sci, Dept Cosmet Sci Natl Taiwan Univ, Dept Chem Engn Natl Taiwan Univ, Dept Mat Sci & Engn
關鍵字:	Cellulose acetate propionate (CAP) Poly(butylene terephthalate) (PBT) Compatibilizer Partially miscible Nanofiber
日期:	2018-03-06
上傳時間:	2019-11-15 15:48:02 (UTC+8)
出版者:	SPRINGER
摘要:	Blends of poly(butylene terephthalate) (PBT) and cellulose acetate propionate (CAP) were found to be immiscible. In order to improve the interfacial strength and miscibility of the PBT/CAP blends, a low-molecular-weight poly(ethylene glycol) (PEG) was thus pre-mixed with the CAP to form the P-CAP mixture. It was then blended with the PBT up to 15 wt% using a twin-screw extruder to prepare the PBT/P-CAP blends, and subsequently processed into the films and fibers by compression-molding and melt-spinning, respectively. The thermal and dynamic mechanical analyses suggested that the PBT and CAP became partially miscible and the interfacial strength was thus improved in the PBT/ PCAP blends, owing to the addition of PEG. The PEG was not only miscible with the CAP but also with the PBT, and it served as a plasticizer as well as a compatibilizer. From the observation of the fractured surface of the PBT/P-CAP films, the PBT component was present as dispersed particles in the P-CAP matrix with size ranging from 1.4 to 3.0 mu m; yet it became nanofiber in the spun fibers. Successful fibers of the PBT/ P-CAP blends with an average diameter of 20 mu m could be spun, where the tensile strength and elongation at break were in the range of 0.6-0.7 g/denier and 12-16%, respectively. Finally, the ultra-fine PBT nanofibers with diameters in the range of 50-70 nm were observed after removing the P-CAP matrix with acetone from the fibers, owing to the formation of PBT nanofibers during spinning and orientation processes. This method thus could successfully produce nano-scale PBT fibers with fineness comparable with the nanofibers developed via electrospinning technology.
link:	http://dx.doi.org/10.1007/s10965-018-1487-5
關聯:	European Radiology, v.25, n.4, 88
顯示於類別:	[化妝品應用與管理系(所)] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	1286	檢視/開啟

在CNU IR中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....