    標題: Preparation and characterization of biodegradable acrylic acid grafted poly(ɛ-caprolactone)/chitosan blends
    作者: Yen Wang
    Jiang-F. Yang
    貢獻者: Department of Chemical Engineering, Tunghai University
    關鍵字: polycaprolactone
    chitosan
    biodegradable
    solution blended film
    日期: 2008-07
    上傳時間: 2017-12-04 16:01:22 (UTC+8)
    摘要: The objective of this work was to study the effect of blending chitosan chitosan (CS) with poly ( ɛ-caprolactone) (PCL) and acrylic acid grafted PCL (PCLgAA) on their biomechanical properties. Blend films with different compositions were prepared from acetic acid in order to improve the properties of chitosan and obtain new fully biodegradable materials. The blends were characterized by Fourier transform infrared analysis (FTIR), differential scanning calorimetry (DSC), wide-angle x-ray diffraction (WAXD), and tensile tests. FTIR results showed that intermolecular hydrogen bonds existed between these components in the blends, and the hydrogen bonds were mainly between carbonyls of PCL and amino groups of chitosan. In addition, the amino groups were shown to form amide or imide linkage with the grafted carboxylic acid in PCLgAA. The melting temperatures, cold crystallization and crystallinity of the PCL component decreased with the increase in chitosan content. Blending chitosan with both PCL and PCLgAA suppressed the crystallization of the polymeric component. Although the crystal structure of PCL component was not changed, the crystallization of the blends was affected because of the existence of hydrogen bonds between two components, which was proved by WAXD results. Finally, the ductility of CS was improved during tensile testing when blended with both polymers.
    關聯: 第五屆海峽化學、生物及材料研討會，起迄日：2008/07/21-2008/07/22，地點：嘉南藥理科技大學
    显示于类别:[藥理學院] 2008第五屆海峽化學、生物及材料研討會

    文件中的档案:

    档案 描述 大小格式浏览次数
    M01.pdf342KbAdobe PDF320检视/开启


    在CNU IR中所有的数据项都受到原著作权保护.

    TAIR相关文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈