鈉型離子交換薄膜之製備與滲透蒸發之研究

Chia Nan University of Pharmacy & Science Institutional Repository > 嘉南學報 > 33 期 (2007) > Item 310902800/19089

請使用永久網址來引用或連結此文件: https://ir.cnu.edu.tw/handle/310902800/19089

標題:	鈉型離子交換薄膜之製備與滲透蒸發之研究 Sodium Ion Exchanged Membrane for Pervaporation Application
作者:	陳世雄劉瑞美何明憲張錦松洪睦雅施琦玉黃政賢
貢獻者:	環境工程與科學系環境資源管理學系
關鍵字:	鈉離子交換薄膜乙醇-水混合液滲透蒸發膨潤特性 Sodium ion exchanged membranes Ethanol-water mixtures Pervaporation Degree of swelling
日期:	2007
上傳時間:	2009-04-12 09:57:15 (UTC+8)
摘要:	本研究之目的在於以氫氧化鈉作為鈉離子來源，製備鈉離子化交換薄膜以提升高分子膜之滲透蒸發分離性能。研究中鈉離子化交換薄膜之滲透蒸發性能強烈受鈉離子含量與取代程度之影響，當離子含量低時，離子交換膜選擇性高達1000以上且透過率與未取代高分子薄膜相當，鈉離子取代度提高則其薄膜之膨潤度增大，離子交換膜選擇性降低，研究中亦顯示薄膜中溶質吸附組成與鈉離子取代程度關係不大。研究中亦發現高溫與低乙醇濃度操作條件下薄膜之選擇性具良好選擇性。由本實驗之結果發現鈉離子化交換膜能有效提升高分子膜之滲透蒸發性能，且於低乙醇與高溫操作下分離性能良好。 The purpose of this study focused on the preparation of sodium ion exchanged membranes and their application on pervaporation. The separation performance of ion exchanged membranes was strongly influenced by the sodium ion content in membranes and degree of substitution of ion in membranes. The separations of ion exchanged membranes own the separation factor above 1000 while the lower ion content in membranes. The increase in the degree of swelling was contributed by the ion hydration of sodium and ethanol swelling in feed solution. The swelling properties decreased the permselectivity og ion exchanged membranes. The permeate content shows the less independent on the degree of ion substitution. In this study, the low ethanol concentration and high operating temperature benefited the permselectivity and permeation. The results showed that the sodium ion exchanged membranes enriched the membranes separation performances and the low ethanol concentration and lowing temperature operation lead to a good separation performance.
關聯:	嘉南學報(科技類) 33期：p.153-166
顯示於類別:	[嘉南學報] 33 期 (2007) [環境工程與科學系(所)] 期刊論文 [環境資源管理系(所)] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
v33_153_166.pdf		625Kb	Adobe PDF	904	檢視/開啟

在CNU IR中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....