    標題: 觸媒濕式氧化反應處理水溶液中污染物之研究
    作者: 陳煜斌
    貢獻者: 環境工程與科學系
    關鍵字: 擔體觸媒
    Supported catalyst
    觸媒濕式過氧化反應
    含酚廢水
    觸媒再生
    Catalytic wet peroxide oxidation (CWPO)
    Phenolic wastewater
    日期: 2007
    上傳時間: 2008-05-13 14:28:57 (UTC+8)
    出版者: 台南縣：嘉南藥理科技大學環境工程與科學系
    摘要: 本研究利用γ型三氧化二鋁(γ-Al2O3)作為擔體，合成各種不同金屬觸媒，在添加過氧化氫之狀態下進行觸媒濕式過氧化反應(Catalytic Wet Peroxide Oxidation，CWPO)，藉由分析酚轉化率與COD去除率，評估各種觸媒對於含酚廢水濕式過氧化反應之催化效能。本研究所合成之金屬觸媒包括Cu、Mn、Co、Cr和Ni，添加量固定為5wt%。研究結果顯示以銅合成之觸媒作為觸發過氧化氫生成氫氧自由基 (free radicals，OH․)之效果最佳，在反應條件為：酚濃度500mg/L、觸媒添加量1.0g/L、過氧化氫添加量1200mg/L、起始pH=3、反應溫度40℃時，5wt%Cu/γ-Al2O3觸媒反應三小時之酚轉化率及COD去除率分別約80%及32%；為了增加觸媒之催化活性與耐用性，本研究合成含浸量為15-5wt%之Ce-Cu/γ- Al2O3觸媒，在觸媒添加量1.5g/L，過氧化氫1200ppm，反應溫度40℃，起始pH=3，酚濃度500mg/L之反應情況下，對酚之去除效率在3小時內可達90%以上，化學需氧量的去除率亦可達38%。使用過後之Ce-Cu/γ- Al2O3觸媒經再生後，重複測試並與新鮮觸媒作比較，其催化效率雖然降低，但再生效能優於銅擔體觸媒，故鈰-銅擔體觸媒比銅觸媒有較優之活性與耐用性。
    Catalysts with various metals(Cu、Mn、Co、Cr and Ni) supported on γ-Al2O3 were used to implement the catalytic wet peroxide oxidation (CWPO) of phenolic wastewater. Via rates of phenol conversion and COD removal, performance of the catalysts was evaluated to screen for the optimal one. With fixed amount of metal (5wt%), the Cu/γ-Al2O3 performed best because it catalyzes H2O2 to create effective free radicals. At the conditions of 500mg/L phenol concentration, 1.0 g/L catalyst loading, 1200mg/L H2O2, initial pH 3 and 40℃, the phenol conversion and COD removal after 3 hrs reaction were 80% and 32%, respectively. On the other hand, the 15-5wt% Ce-Cu/γ-Al2O3 prepared in this study was found to be more active and durable than Cu/γ-Al2O3 catalyst tested. At the conditions of 1.5 g/L catalyst loading, 1200mg/L H2O2, initial pH 3 and 40℃, 500mg/L phenol could attain 90% phenol conversion and 38% COD removal after 3hours CWPO reaction. Though the activity of regenerated catalysts, including Ce-Cu/γ-Al2O3 and Cu/γ-Al2O3 catalysts, was lower than that of fresh ones, it was found that regenerated Ce-Cu/γ-Al2O3 had higher performance than the regenerated Cu/γ-Al2O3 catalyst tested.
    關聯: 計畫編號 : CN9647
    显示于类别:[環境工程與科學系(所)] 校內計畫

    文件中的档案:

    档案 描述 大小格式浏览次数
    96CN9647.pdf272KbAdobe PDF913检视/开启


    在CNU IR中所有的数据项都受到原著作权保护.

    TAIR相关文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈